LEXAN™ XHT2141 resin
Polycarbonate
SABIC Innovative Plastics
产品说明:
XHT2141 is a high flow, high heat polycarbonate copolymer. It isavailable in a range of opaque and limited transparent colors.
物性信息:
物理性能 | 额定值 | 单位制 | 测试方法 |
---|
比重 | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
熔流率(熔体流动速率) (330°C/2.16 kg) | 46 | g/10 min | ASTM D1238 |
溶化体积流率(MVR) (330°C/2.16 kg) | 43.0 | cm³/10min | ISO 1133 |
收缩率 - 流动 (3.20 mm) | 0.60 到 0.90 | % | 内部方法 |
吸水率 |
|
| ISO 62 |
饱和, 23°C | 0.30 | % | ISO 62 |
平衡, 23°C, 50%RH | 0.23 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|
拉伸模量 |
|
|
|
-- 1 | 2600 | MPa | ASTM D638 |
-- | 2600 | MPa | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 2 | 70.0 | MPa | ASTM D638 |
屈服 | 70.0 | MPa | ISO 527-2/50 |
断裂 3 | 60.0 | MPa | ASTM D638 |
断裂 | 60.0 | MPa | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 4 | 6.5 | % | ASTM D638 |
屈服 | 6.5 | % | ISO 527-2/50 |
断裂 5 | 90 | % | ASTM D638 |
断裂 | 90 | % | ISO 527-2/50 |
弯曲模量 |
|
|
|
50.0 mm跨距 6 | 2550 | MPa | ASTM D790 |
-- 7 | 2450 | MPa | ISO 178 |
弯曲应力 |
|
|
|
-- | 100 | MPa | ISO 178 |
屈服, 50.0 mm跨距 8 | 110 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|
简支梁缺口冲击强度 9 |
|
| ISO 179/1eA |
-30°C | 9.0 | kJ/m² | ISO 179/1eA |
23°C | 12 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 10 |
|
| ISO 179/1eU |
-30°C | 无断裂 |
| ISO 179/1eU |
23°C | 无断裂 |
| ISO 179/1eU |
悬壁梁缺口冲击强度 |
|
|
|
-30°C | 75 | J/m | ASTM D256 |
23°C | 120 | J/m | ASTM D256 |
-30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
-30°C 12 | 10 | kJ/m² | ISO 180/1A |
23°C 13 | 11 | kJ/m² | ISO 180/1A |
23°C 14 | 10 | kJ/m² | ISO 180/1A |
无缺口伊佐德冲击强度 15 |
|
| ISO 180/1U |
-30°C | 无断裂 |
| ISO 180/1U |
23°C | 无断裂 |
| ISO 180/1U |
装有测量仪表的落镖冲击 (23°C, TotalEnergy) | 68.0 | J | ASTM D3763 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|
载荷下热变形温度 |
|
|
|
0.45 MPa, 未退火, 3.20mm | 155 | °C | ASTM D648 |
0.45 MPa, 未退火, 64.0mm 跨距 16 | 155 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火, 3.20mm | 145 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm跨距 17 | 142 | °C | ISO 75-2/Af |
维卡软化温度 |
|
|
|
-- | 161 | °C | ASTM D1525 18 |
-- | 160 | °C | ISO 306/B50 |
-- | 162 | °C | ISO 306/B120 |
Ball Pressure Test (125°C) | Pass |
| IEC 60695-10-2 |
线形热膨胀系数 |
|
| ASTM E831, ISO 11359-2 |
流动 : -40 到40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
横向 : -40 到40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
导热系数 (25°C) | 0.20 | W/m/K | ASTM C177 |
RTI Elec | 150 | °C | UL 746 |
RTI Imp | 130 | °C | UL 746 |
RTI | 150 | °C | UL 746 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|
表面电阻率 | > 1.0E+17 | ohms | ASTM D257 |
体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
介电强度 (3.20 mm, in Oil) | 23 | kV/mm | ASTM D149 |
相比耐漏电起痕指数(CTI) | PLC 3 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 0 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
补充信息 | 额定值 | 单位制 | 测试方法 |
---|
Metallized Haze Onset | 155 | °C | 内部方法 |
注射 | 额定值 | 单位制 |
|
---|
干燥温度 | 125 | °C |
|
干燥时间 | 4.0 到 6.0 | hr |
|
建议的Zui大水分含量 | 0.020 | % |
|
建议注射量 | 40 到 60 | % |
|
料筒后部温度 | 270 到 305 | °C |
|
料筒中部温度 | 280 到 325 | °C |
|
料筒前部温度 | 290 到 335 | °C |
|
射嘴温度 | 285 到 330 | °C |
|
加工(熔体)温度 | 290 到 335 | °C |
|
模具温度 | 85.0 到 130 | °C |
|
背压 | 0.300 到 0.700 | MPa |
|
螺杆转速 | 40 到 90 | rpm |
|
排气孔深度 | 0.025 到 0.080 | mm |
|